About HOSOCP, HOSOPM, HOSOCU
Published on:
2020-03-25 15:48
Author:
Ervin
Our registered trademark:
HOSOCU®- for special copper,
HOSOPM® - for No-ferrous metal,
HOSOCP® - for the machining parts.
Below is the table for HOSOCU and HOSOPM
Product |
Brand |
Description and remark |
Density (g/cm3) |
Hardness (HRB) |
Electrical conductivity (%IACS) |
ODS copper |
HOSOCU®150J |
Al2O3 content 0.3% wt. |
8.90 |
70 |
90 |
HOSOCU®150H |
Al2O3 content 1.1% wt. |
8.90 |
80 |
78 |
|
Chromium copper |
HOSOCU®201 |
C18200(Cr 0.6-1%) |
8.90 |
68 |
85 |
Chromium copper |
HOSOCU®205 |
Cr 50%,Cu balance |
7.90 |
90HB |
28 |
Zirconium copper |
HOSOCU®203 |
C15000(Zr 0.2-0.3%) |
8.90 |
65 |
89 |
Chromium Zirconium copper |
HOSOCU®202 |
C18150,CuCrlZr |
8.90 |
75 |
75 |
Beryllium nickel copper |
HOSOCU®301 |
C17510(Be:0.2-0.4%,Ni:1.8-2.8),NBC |
8.90 |
94 |
48 |
Beryllium cobalt copper |
HOSOCU®302 |
C17500(Be:0.2-0.4),Co:1.8-2.5) |
8.90 |
98 |
45 |
Beryllium cobalt copper |
HOSOCU®302J |
C17500(Be:0.35-0.75,Co:1.9-2.2,Ni:1.7-2.2) |
8.90 |
95 |
51 |
Beryllium copper |
HOSOCU®400 |
C17200 |
8.90 |
38HRC |
18 |
No beryllium copper |
HOSOCU®303 |
C18000 Ni:1.8-2.8,Si:0.4-0.8,Cr:0.4-0.8 |
8.90 |
90 |
45 |
Brass |
HOSOCU®500 |
8.90 |
|
20 |
|
Tellurium copper |
HOSOCU®501 |
|
|
|
|
Pure copper |
HOSOCU®600 |
8.90 |
HV85-120 |
|
|
Tungsten copper |
HOSOPM®070 |
0 – group,70 – content of tungsten |
|
|
|
Silver |
HOSOPM®101 |
pure silver |
|
|
|
Tungsten silver |
HOSOPM®170 |
1-group,70 – content of tungsten |
|
|
|
Tungsten carbide copper |
HOSOPM®270 |
2-group,70 –content of tungsten carbide |
|
|
|
Tungsten carbide silver |
HOSOPM®370 |
3-group,70-content of tungsten carbide |
|
|
|
Tungsten nickel copper |
HOSOPM®490 |
4-group, 90-content of tungsten |
|
|
|
Tungsten nickel iron |
HOSOPM®590 |
5-group,90-content of tungsten |
|
|
|
Hafnium |
HOSOPM®700 |
>= 99.99 |
13.31 |
|
|
Zirconium |
HOSOPM®701 |
>=99.99 |
6.49 |
|
|
Ceramics |
HOSOPM®703 |
Alumina Ceramic |
|
|
|
Iron |
HOSOPM®718 |
Soft type |
8.90 |
80-90 HRB |
|
Molybdenum |
HOSOPM®800 |
ASTM 387,Mo> 99.95% |
10.12 |
90HRB |
30 |
TZM |
HOSOPM®802 |
Mo, Ti, Cr alloy |
10.20 |
25HRC |
28 |
Moly copper |
HOSOPM®870 |
8-group, 70-content of molybdenum |
9.80 |
69.0 |
37.0 |
Tungsten |
HOSOPM®900 |
W, Tungsten, rein tungsten |
19.00 |
30HRC |
30 |
Rhenium tungsten |
HOSOPM®901 |
High temperature |
19.16 |
40HRC |
|
Thorium tungsten |
HOSOPM®902 |
Th2O3>1.8%,W: balance,ISO6848 |
|
|
|
Yttrium tungsten |
HOSOPM®903 |
17.84 |
40-43HRC |
|
|
Cerium tungsten |
HOSOPM®904 |
18.50 |
38-40 HRC |
|
|
YG6 |
HOSOPM®906 |
cobalt 6%,grain size: 2um |
14.80 |
89 |
|
YG6X |
HOSOPM®906X |
Grain size: 0.8um |
14.90 |
91 |
|
YG6A |
HOSOPM®906A |
Super hard |
14.90 |
78HRC |
|
Zirconated tungsten |
HOSOPM®907 |
ZrO: 0.7-0.9%,W: balance |
18.90 |
40-43HRC |
|
YG8 |
HOSOPM908 |
cobalt 8% |
14.70 |
93HRA |
|
YG10 |
HOSOPM910 |
cobalt 10% |
14.30 |
75HRC |
|
YG15 |
HOSOPM915 |
cobalt 15% |
13.95 |
90HRA |
|
YG20 |
HOSOPM916 |
Cobalt 20% |
14.00 |
86-87 |
|
Lanthanum tungsten |
HOSOPM®920 |
La 2% |
18.50 |
35-39HRC |
|
Lanthanum tungsten |
HOSOPM®921 |
La 1.5% |
|
|
|
Lanthanum tungsten |
HOSOPM®922 |
La 1% |
19.00 |
40HRC |
28 |